Intergranular corrosion of Cu-Al-Ni alloy in 0.5 mol dm−3 H2SO4 solution / Ladislav Vrsalović, Senka Gudić, Lana Terzić, Ivana Ivanić, Stjepan Kožuh, Mirko Gojić, Emeka Emmanuel Oguzie.
Sažetak

The corrosion behaviour of Cu-Al-Ni alloy in 0.5 mol dm–3 H2SO4 solution was investigated by electrochemical methods including open circuit potential measurement, electrochemical impedance spectroscopy measurements, linear and potentiodynamic polarization. Measurements were performed in 0.5 mol dm–3 H2SO4 at temperatures 20 and 40 °C. After polarization testing, corroded electrode surfaces were ultrasonically cleaned in deionized water and examined by light and scanning electron microscopy, while the elemental composition at individual points of the alloy surface was determined by EDS analysis. The results of the investigations revealed the occurrence of intergranular corrosion on the Cu-Al-Ni surface, which became more pronounced with increasing temperature.; Korozijsko ponašanje Cu-Al-Ni legure u 0,5 mol dm–3 H2SO4 otopini ispitivano je elektrokemijskim metodama kao što su mjerenje potencijala otvorenog strujnog kruga, mjerenje metodom elektrokemijske impedancijske spektroskopije, linearne i potenciodinamičke polarizacije. Mjerenja su provedena u 0,5 mol dm–3 H2SO4 pri temperaturama od 20 i 40 °C. Nakon polarizacijskih mjerenja korodirane površine elektroda ultrazvučno su očišćene u deioniziranoj vodi i ispitane svjetlosnim i pretražnim elektronskim mikroskopom, dok je elementarni sastav na pojedinim točkama na površini određen EDS analizom. Rezultati ispitivanja pokazali su da dolazi do interkristalne korozije na površini Cu-Al-Ni legure, čiji intenzitet raste s povećanjem temperature elektrolita.